All Products
-
نبيلةويلك مسؤول جدًا عنا، وقد أنهوا بضائعنا العاجلة في أقصر وقت ممكن، شكرًا حقًا، لقد قمنا أيضًا بفحص البضائع قبل التسليم، والجودة نحن أيضًا راضون جدًا، وسمك الحجم واللون يتماشى مع متطلباتي. -
EdwardWilke is very professional, they are really helpful and reliable. The delivery time is really quick, and checked the coils with good quality. Look forward to cooperating with them soon!
-
JoyceWe asked a third party to test these goods, and the quality surprised us. The second batch of orders is already under negotiation. Thank you Fiona for your professional service!
Contact Person :
Fiona Qin
Phone Number :
+8618112493792
Whatsapp :
+8618112493792
Mn13 A36 Wear Resistant Steel Plate Mild ASTM Carbon Steel Sheet Plate
| Place of Origin | China |
|---|---|
| Brand Name | Tisco |
| Certification | ISO MTC SGS |
| Model Number | Wear Resistant Steel Plate |
| Minimum Order Quantity | 1Ton |
| Price | Negotiation |
| Packaging Details | Standard seaworthy packing or customer required |
| Delivery Time | 10-15 days after deposit |
| Payment Terms | T/T, L/C, Western Union |
| Supply Ability | 5000 Ton per Month |
Contact me for free samples and coupons.
Whatsapp:0086 18588475571
Wechat: 0086 18588475571
Skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xProduct Details
| Name | Mn13 Wear Resistant Steel Plate A36 Mild Steel Plate | Thickness | 0.3mm-260mm |
|---|---|---|---|
| Width | 1m,2m | Length | 5800mm,6000,mm12000mm |
| Technique | Hot Rolled | Surface Treatment | Clean, Blasting And Painting According To Customer Requirement |
| Grade | S 450 550 500 600 | Tolerance | ±1%, 1%-3% |
| High Light | Mn13 Wear Resistant Steel Plate,A36 Wear Resistant Steel Plate,Mn13 ASTM Steel Sheet |
||
Product Description
Mn13 Wear Resistant Steel Plate A36 Mild Steel Plate ASTM Carbon Steel Sheet
Wear resistant steel plate NM400, NM450, NM500 etc. widely used in construction machinery, environmental protection machinery,
metallurgical machinery, loader, blade plate, side blade plate.
Product Description :
|
|
chemical composition
|
|||||||||
|
Grade
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Mo
|
T
|
|
≤
|
|||||||||
|
NM300
|
0.23
|
0.70
|
1.60
|
0.025
|
0.015
|
0.70
|
0.50
|
0.40
|
0.050
|
|
NM360
|
0.25
|
0.70
|
1.60
|
0.025
|
0.015
|
0.80
|
0.50
|
0.50
|
0.050
|
|
NM400
|
0.30
|
0.70
|
1.60
|
0.025
|
0.010
|
1.0
|
0.70
|
0.50
|
0.050
|
|
NM450
|
0.35
|
0.70
|
1.70
|
0.025
|
0.010
|
1.1
|
0.80
|
0.55
|
0.050
|
|
NM500
|
0.38
|
0.70
|
1.70
|
0.020
|
0.010
|
1.2
|
1.00
|
0.65
|
0.050
|
|
Mechanical property |
||||
|
Grade
|
Thickness(mm)
|
tensile strength(MPa)
|
Elongation A(%)
|
Surface Brinell hardness(HBW)
|
|
NM300
|
≤80
|
≥1000
|
≥14
|
270-330
|
|
NM360
|
≤80
|
≥1100
|
≥12
|
330-390
|
|
NM400
|
≤80
|
≥1200
|
≥10
|
370-430
|
|
NM450
|
≤80
|
≥1250
|
≥7
|
420-480
|
|
NM500
|
≤70
|
-
|
-
|
≥470
|
|
Grade comparison
|
|
|
GB
|
NM300,NM360,NM400,NM450,NM500
|
|
SS
|
400,450,500,600
|
|
DIN
|
XAR400,XAR450,XAR500,XAR600,Dillidur400,Dillidur500
|
|
NBN
|
QUARD400,QUARD450,QUARD500
|
|
NF
|
FORA400,FORA500,Creusabro4800,Creusabro8000
|
|
JIS
|
JFE-EH360, JFE－EH400,JFE－EH500,WEL-HARD400,WEL-HARD500
|
|
SFS
|
RAEX400,RAEX450,RAEX500
|
Structural Features :
1.Wear-resisting steel plate is composed of low carbon steel plate and alloy wear-resisting layer. When working, the matrix provides comprehensive properties such as strength, toughness and plasticity of resisting external forces, and the alloy wear-resistant layer provides wear-resistant properties that meet the requirements of specified working conditions.
2.Wear-resisting steel alloy wear-resisting layer and base plate are metallurgical combination. By means of special equipment and automatic welding process, the high-hardness self-protecting alloy wire is uniformly welded on the substrate, and the composite layers are one to two or even more. In the composite process, due to the different shrinkage ratio of the alloy, uniform transverse cracks appear, which is a significant feature of the wear-resistant steel plate.
3.The wear resistant layer of the alloy is mainly chromium alloy, while manganese, molybdenum, niobium, nickel and other alloys are added. The microhardness of carbide can reach above hv1700-2000, and the surface hardness can reach hrc58-62. Carbide alloy has a strong stability at high temperature, maintain a high hardness, but also has a good oxidation resistance, within 500℃ completely normal use.
4.The wear-resistant layer has narrow channel (2.5-3.5mm), wide channel (8-12mm), curve (S, W), etc. It is mainly composed of chromium alloy, while manganese, molybdenum, niobium, nickel, boron and other alloy components are added. With 40-60% carbide content, the microhardness can reach above HV1700 and the surface hardness can reach hrc58-62.